Lihlahisoa tsa tšepe tse bohlooho kaho lahla hloboleMochini o nepahetseng oa CNCgditsamaiso.
Bokhoni ba Sand Casting e entsoeng ka letsoho:
• Boholo ba Boholo: 1,500 mm × 1000 mm × 500 mm
• Boima ba Boima: 0,5 kg - 500 kg
• Bokhoni ba Selemo: lithane tse 5,000 - lithane tse 6,000
• Mamello: Ka Kopo kapa Maemo (ISO8062-2013 kapa Chinese Standard GB/T 6414-1999)
• Lisebelisoa tsa Mold: Ho Lahlela Lehlabathe le Letala, Ho Rala Lehlabathe la Shell Mold.
Bokhoni ba ho Lahlela Lehlabathe ka Mechini ea Molding e Ikemetseng:
• Boholo ba Boholo: 1,000 mm × 800 mm × 500 mm
• Boima ba Boima: 0,5 kg - 500 kg
• Bokhoni ba Selemo: lithane tse 8,000 - lithane tse 10,000
• Mamello: Ka Kopo Kapa Ho ea ka Maemo (ISO8062-2013 kapa Chinese Standard GB/T 6414-1999)
• Lisebelisoa tsa Mold: Ho Lahlela Lehlabathe le Letala, Resin Coated Sand Shell Molding Casting.
Thesetsi sa ho lahla hloboho RMC e na le laboratori e feletseng ea metallurgical ho fumana litšobotsi tsa lik'hemik'hale le tsa mechine tsa ho qhibiliha ka 'ngoe le ho hlahloba boemo ba metallurgic ea tšepe e qhibilihisitsoeng pele e tšolloa. Li-microsections li hlahlojoa ka tlas'a microscope ho fumana boitsebiso ba ho qetela. Haeba ho khonahala kapa ho hlokahala, re ka fana ka Setifikeiti sa 3.1 bakeng sa karolo ka 'ngoe ea thomello ho latela tlhoko ea bareki.
Lihlahisoa tsa lehlabatheka sebeletsa kaliindasteri tse ngatajoalo ka Meropa, Gear, Gear Housing, Mechine ea Merafo, Mounting Block, Hydraulic Pressure Pump, Bearing Seat, Support Ring, Idler Wheel, Clamp, Mounting Bracket, Wheel Hub, Wedge Socket, Track Pad Bakeng sa Lisebelisoa tsa Morafo, Hydraulic Rod Yoke.. .joalo-joalo.
| Mechanical Properties of Grey Cast Iron | |||||||
| Ntho ho latela DIN EN 1561 | Lekanya | Yuniti | EN-GJL-150 | EN-GJL-200 | EN-GJL-250 | EN-GJL-300 | EN-GJL-350 |
| EN-JL 1020 | EN-JL 1030 | EN-JL 1040 | EN-JL 1050 | EN-JL 1060 | |||
| Matla a tšepe | Rm | MPA | 150-250 | 200-300 | 250-350 | 300-400 | 350-450 |
| 0.1% Matla a Puno | Rp0,1 | MPA | 98-165 | 130-195 | 165-228 | 195-260 | 228-285 |
| Elongation Matla | A | % | 0,3 - 0,8 | 0,3 - 0,8 | 0,3 - 0,8 | 0,3 - 0,8 | 0,3 - 0,8 |
| Matla a Khatellang | σdB | MPa | 600 | 720 | 840 | 960 | 1080 |
| 0,1% Matla a Khatellang | σd0,1 | MPa | 195 | 260 | 325 | 390 | 455 |
| Flexural Matla | σbB | MPa | 250 | 290 | 340 | 390 | 490 |
| Schuifspanning | σaB | MPa | 170 | 230 | 290 | 345 | 400 |
| Ho Shear Khatello | TtB | MPa | 170 | 230 | 290 | 345 | 400 |
| Li-module tsa elasticity | E | GPA | 78-103 | 88-113 | 103 - 118 | 108 - 137 | 123 - 143 |
| Nomoro ea Poisson | v | - | 0,26 | 0,26 | 0,26 | 0,26 | 0,26 |
| Ho thatafala ha Brinell | HB | 160-190 | 180 - 220 | 190-230 | 200 - 240 | 210 - 250 | |
| Ductility | σbW | MPa | 70 | 90 | 120 | 140 | 145 |
| Ho fetoha ha tsitsipano le khatello | σzdW | MPa | 40 | 50 | 60 | 75 | 85 |
| Matla a Qhoba | Klc | N/mm3/2 | 320 | 400 | 480 | 560 | 650 |
| Botenya | g/cm3 | 7,10 | 7,15 | 7,20 | 7,25 | 7,30 | |
Cast iron ke motsoako oa tšepe oa carbon cast o nang le likarolo tse ling tse entsoeng ka ho qhibilihisa tšepe ea kolobe, likotoana le litlatsetso tse ling. Bakeng sa phapang ho tloha ho tšepe le tšepe e entsoeng ka tšepe, tšepe e entsoeng ka tšepe e hlalosoa e le alloy e entsoeng ka carbon content (min 2.03%) e tiisang ho tiea ha mohato oa ho qetela ka phetoho ea eutectic. Ho ipapisitsoe le lintlha tsa lik'hemik'hale, litšepe tse entsoeng ka tšepe li ka ba tse sa kopaneng kapa tsa alloyed. Mefuta e mengata ea litšepe tse kopantsoeng e pharaletseng haholo, 'me e na le likarolo tse ngata tse tloaelehileng, tse kang silicon le manganese, kapa litlatsetso tse khethehileng, tse kang nickel, chromium, aluminium, molybdenum, tungsten, koporo, vana-dium, titanium, hammoho. ba bang. Ka kakaretso, tšepe e entsoeng ka tšepe e ka aroloa ka tšepe e bohlooho, tšepe ea ducitle (nodular iron), tšepe e tšoeu e entsoeng ka tšepe, tšepe e entsoeng ka graphite e kopantsoeng le tšepe e bonolo.